Molecular Formula: TiNbCT_x

Storage Conditions: Store refrigerated (4°C) or in a vacuum or inert environment for 2-6 months.

Product Introduction

Double transition-metal MXene TiNbCT_x is a member of the MXene family, featuring a typical two-dimensional layered structure terminated with surface groups such as hydroxyl (-OH), fluorine (-F), or oxygen (=O), collectively referred to as "T_x." This unique combination of transition metals endows TiNbCT_x with exceptional properties, including high electrical conductivity, excellent mechanical strength, and chemical stability. The material's tunable surface chemistry enhances its hydrophilicity and reactivity, making it highly suitable for applications in energy storage, catalysis, electromagnetic shielding, and biosensors.

Product Characteristics

The product appears as a brown powder or dark blue liquid.
The product is etched by lithium fluoride/hydrochloric acid (LiF/HCl) system, which can significantly improve the stability of the material.
The concentration of the product is adjustable, and the flake size is controllable.
The liquid should be stored refrigerated (0-4 °C), while the powder should be stored in a vacuum-dried or inert environment.

Performance Parameters

Product Type	Multilayer TiNbCT_x Powder	Monolayer TiNbCT_x Powder	Monolayer TiNbCT_x Aqueous Solution	Monolayer TiNbCT_x Flexible Film
Catalog Number	NM-MX067	NM-MX068	NM-MX069	NM-MX070
Etching Process	LiF/HCl etching	LiF/HCl etching + Intercalating agent-induced delamination	LiF/HCl etching + Intercalating agent-induced delamination	LiF/HCl etching + Intercalating agent-induced delamination
Color	Brown	Copper brown	Dark blue	Copper brown
Multilayer Size	2-20μm	/	/	/
Monolayer Size	/	200-1000 nm	200-1000 nm	1000-10000 nm
Number of Layers	Multilayer	≤5 layers	≤5 layers	≤5 layers
Concentration	/	/	1-10 mg/mL (customizable)	/
Conductivity	10-100 S/cm	800±500 S/cm	800±500 S/cm	800±500 S/cm
Surface Groups	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl