Multilayer/Monolayer Ti₂VC₂T_x

Molecular Formula: Ti₂VC₂T_x

Storage Conditions: Store refrigerated (4°C) or in a vacuum or inert environment for 2-6 months.

Product Introduction

Double transition-metal MXene Ti₂VC₂T_x is a two-dimensional material composed of titanium (Ti), vanadium (V), and carbon (C), with surface terminations (T_x) typically including =O, -OH, or -F groups. This layered carbide structure exhibits unique properties stemming from its dual transition-metal composition, offering a balance of high electrical conductivity, mechanical strength, and tunable surface chemistry. The presence of vanadium introduces additional redox activity compared to single-metal MXenes, enhancing its electrochemical performance in applications such as energy storage, catalysis, and sensing.

Product Characteristics

The product appears as a dark purple powder or green liquid.
The product is prepared through lithium fluoride/hydrochloric acid (LiF/HCl) etching and exhibits excellent antioxidant properties.
The concentration of the product is adjustable, and the flake size is controllable.
The product introduces vanadium atoms at the transition metal sites, which significantly improves the energy storage performance.
The liquid should be stored refrigerated (0-4 °C), while the powder should be stored in a vacuum-dried or inert environment.

Performance Parameters

Product Type	Multilayer Ti₂VC₂T_x Powder	Monolayer Ti₂VC₂T_x Powder	Monolayer Ti₂VC₂T_x Aqueous Solution	Monolayer Ti₂VC₂T_x Flexible Film
Catalog Number	NM-MX071	NM-MX072	NM-MX073	NM-MX074
Etching Process	LiF/HCl etching	LiF/HCl etching	LiF/HCl etching	LiF/HCl etching
Color	Dark purple	Dark purple	Green	Dark purple
Multilayer Size	2-20μm	/	/	/
Monolayer Size	/	200-1000 nm	200-1000 nm	1000-10000 nm
Number of Layers	Multilayer	≤5 layers	≤5 layers	≤5 layers
Concentration	/	/	1-10 mg/mL (customizable)	/
Conductivity	10-100 S/cm	1500±500 S/cm	1500±500 S/cm	1500±500 S/cm
Surface Groups	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl