Multilayer Clay-like Ti₃C₂T_x (LiF/HCl Etching)

Molecular Formula: Ti₃C₂T_x

Molecular Weight: 167.6

Purity: ≥98%

Etching Process: LiF/HCl etching

Element Content: Ti (57.8%); C (40.2%); Al (≤2%)

Storage conditions: Vacuum refrigerated storage (4°C) for 6 months

Online Inquiry Contact Us

Product Introduction

Multilayer clay-like Ti₃C₂T_x is a unique form of Mxene material, characterized by its layered, clay-like structure. This material is synthesized through a mild etching process using a lithium fluoride/hydrochloric acid (LiF/HCl) system, which differentiates it from the traditional hydrofluoric acid (HF) etching methods commonly used for Ti₃C₂T_x.

Multilayer clay-like Ti₃C₂T_x exhibits high conductivity, mechanical strength, and chemical stability. Its unique two-dimensional structure and surface functionalities make it an ideal choice for various applications, including energy storage (such as supercapacitors and batteries), sensors, and catalysis. Furthermore, the material's hydrophilicity allows for easy dispersion in aqueous solutions, further enhancing its potential for applications in energy and environmental technologies.

Product Characteristics

The product has a dark purple color.
The product is a two-dimensional layered material with a multi-layer structure, where the layers are bonded by van der Waals forces.
Compared to HF etching, the LiF/HCl etching system can improve conductivity and increase hydrophilicity.
The monolayer exfoliation method includes low-power (80-200W) ultrasound or manual shaking.
The product has a long shelf life and should be stored in a vacuum or an inert environment.

Performance Parameters

Parameters	Catalog Number
Parameters	NM-MX003	NM-MX004
Etching Material Mesh Size	~200 mesh	~400 mesh
Size After Etching	2-50 μm	2-20 μm
Color	Dark purple	Dark purple
Conductivity	1000±500 S/cm	1000±500 S/cm
Specific Surface Area	20±5 m²/g	20±5 m²/g
Density	3.43+0.03 g/cm³	3.43+0.03 g/cm³
Water Solubility	Good	Good
Surface Groups	-OH, =O, -F, -Cl	-OH, =O, -F, -Cl